Grey Cast Iron Magnetic Eigenskippen

Grey Iron Fergeliking				Mikrostruktuer (Volume Fractions) (％)
Sina (GB/T 9439)	ISO 185	ASTM A48/A48M	EN 1561	Matrix Struktuer
HT100 (HT10-26)	100	No.20 F11401	EN-GJL-100	Pearlite: 30-70%, grof flakes; Ferriet: 30-70%; Binêre fosfor eutektysk: ＜7％
HT150 (HT15-33)	150	No.25A F11701	EN-GJL-150	Pearlite: 40-90%, medium grouwe flakes; Ferriet: 10-60%; Binêre fosfor eutektysk: ＜7％
HT200 (HT20-40)	200	No.30A F12101	EN-GJL-200	Pearlite: ＞95％, medium flakes; Ferrite ＜5％; Binary Phosphorus Eutectic＜4％
HT250 (HT25-47)	250	No.35A F12401 No.40A F12801	EN-GJL-250	Pearlite: ＞98％ medium tinne flakes; Binêre fosfor eutektysk: ＜2％
HT300 (HT30-54)	300	No.45A F13301	EN-GJL-300	Pearlite: ＞98％ medium tinne flakes; Binêre fosfor eutektysk: ＜2％
HT350 (HT35-61)	350	No.50A F13501	EN-GJL-350	Pearlite: ＞98％ medium tinne flakes; Binêre fosfor eutektysk: ＜1％

 

De magnetyske eigenskippen fan griis getten izer fariearje breed, fan lege permeabiliteit en hege twangkrêft oant hege permeabiliteit en lege twangkrêft. Dizze feroarings binne benammen ôfhinklik fan 'e mikrostruktuer fan griis getten izer. It tafoegjen fan legere eleminten om de fereaske magnetyske eigenskippen te krijen wurdt berikt troch de struktuer fan griis getten izer te feroarjen.

Ferrite hat hege magnetyske permeabiliteit en lege hysteresisferlies; pearlite is krekt it tsjinoerstelde, it hat lege magnetyske permeabiliteit en grutte hysteresis ferlies. Pearlite wurdt foarme yn ferrite troch annealing waarmte behanneling, dat kin fergrutsje de magnetyske permeability troch fjouwer kear. It fergrutsjen fan ferrite korrels kin it ferlies fan hysteresis ferminderje. De oanwêzigens fan cementite sil ferminderje de magnetyske flux tichtens, permeability en remanence, wylst it fergrutsjen fan de permeability en hysteresis ferlies. De oanwêzigens fan grof grafyt sil ferminderje de remanence. De feroaring fan A-type grafyt (in flakfoarmige grafyt dy't unifoarm ferdield is sûnder rjochting) nei in D-type grafyt (in fyn krulde grafyt mei in net-rjochtingsferdieling tusken dendriten) kin de magnetyske ynduksje en twangkrêft signifikant ferheegje .

Foardat de net-magnetyske krityske temperatuer berikt wurdt, fergruttet de temperatuerferheging de magnetyske permeabiliteit fan griis getten izer signifikant. It Curiepunt fan suver izer is de α-γ oergongtemperatuer fan 770 °C. As it massapersintaazje silisium 5% is, sil it Curie-punt 730 ° C berikke. De Curie-punttemperatuer fan cementite sûnder silisium is 205-220 °C.

De matrixstruktuer fan meast brûkte graden fan griis getten izer is benammen pearlit, en har maksimale permeabiliteit is tusken 309-400 μH / m.

 

Magnetyske eigenskippen fan griis getten izer
Code of Grey Iron	Gemyske gearstalling (%)
	C	Si	Mn	S	P	Ni	Cr
A	3.12	2.22	0.67	0.067	0.13	＜0.03	0.04
B	3.30	2.04	0.52	0.065	1.03	0.34	0.25
C	3.34	0,83 - 0,91	0,20 - 0,33	0,021 - 0,038	0.025 - 0.048	0.04	＜0.02
Magnetyske eigenskippen		A		B		C
		Pearlite	Ferrite	Pearlite	Ferrite	Pearlite	Ferrite
Carbide koalstof w(%)		0,70	0.06	0.77	0.11	0.88	/
Remanence / T		0.413	0.435	0.492	0.439	0.5215	0.6185
Twangkrêft / A•m-1		557	199	716	279	637	199
Hysteresis ferlies / J•m-3•Hz-1 (B=1T)		2696	-696	2729	1193	2645	938
Magnetyske fjildsterkte / kA•m-1 (B=1T)		15.9	-5.9	8.7	8.0	6.2	4.4
Max. Magnetyske permeabiliteit / μH•m-1		396	1960	353	955	400	1703
Magnetic Field Strength doe't Max. Magnetyske permeabiliteit / A•m-1		637	199	1035	318	1114	239
Resistivity / μΩ•m		0.73	0.71	0.77	0,75	0.42	0.37

 

Hjir yn it folgjende binne de meganyske eigenskippen fan griis getten izer:

Meganyske eigenskippen fan griis getten izer
Artikel volgens DIN EN 1561	Maatregel	Ienheid	EN-GJL-150	EN-GJL-200	EN-GJL-250	EN-GJL-300	EN-GJL-350
			EN-JL 1020	EN-JL 1030	EN-JL 1040	EN-JL 1050	EN-JL 1060
Treksterkte	Rm	MPA	150-250	200-300	250-350	300-400	350-450
0,1% Opbringst Strength	Rp0,1	MPA	98-165	130-195	165-228	195-260	228-285
Ferlinging sterkte	A	%	0,3 – 0,8	0,3 – 0,8	0,3 – 0,8	0,3 – 0,8	0,3 – 0,8
Kompressive sterkte	σdB	MPa	600	720	840	960	1080
0,1% kompresjesterkte	d0,1	MPa	195	260	325	390	455
Flexural sterkte	σbB	MPa	250	290	340	390	490
Schuifspanning	σaB	MPa	170	230	290	345	400
Shear Stress	TtB	MPa	170	230	290	345	400
Modules fan elastisiteit	E	GPa	78 - 103	88 - 113	103 - 118	108 - 137	123 - 143
Poisson nûmer	v	-	0,26	0,26	0,26	0,26	0,26
Brinell hurdens		HB	160 - 190	180 - 220	190 - 230	200 - 240	210 - 250
Duktiliteit	σbW	MPa	70	90	120	140	145
Spanning en druk feroarje	σzdW	MPa	40	50	60	75	85
Breaking Strength	Klc	N/mm3/2	320	400	480	560	650
Tichtheid		g/cm3	7,10	7,15	7,20	7,25	7,30